亚克力树脂 LG化学IF850 聚甲基丙烯酸甲脂
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | 24h | ASTM D-570 | 0.3 | % |
| 物理性能 | 比重 | ASTM D-792 | 1.18 | ||
| 反射指数 | ASTM D-542 | 1.49 | |||
| 透明性 | 3.2mm | ASTM D-1003 | 93 | % | |
| 流动指数 | 230℃,3.8kg | ASTM D-1238 | 12.5 | g/10min | |
| 机械性能 | 拉力 | ASTM D-638 | 690 | Kg/cm2 | |
| 弯曲模数 | ASTM D-790 | 32,000 | Kg/cm2 | ||
| 洛氏硬度 | ASTM D-785 | 89 | M-Scale | ||
| 弯曲强度 | ASTM D-790 | 1,220 | Kg/cm2 | ||
| 延伸率 | ASTM D-638 | 3.0 | % | ||
| 冲击强度 | Izod Notched | ASTM D-256 | 1.6 | kg· cm/cm2 | |
| 模缩系数 | ASTM D995-51 | 0.2-0.6 | % | ||
| 电气性能 | 介电强度 | 4KV/S | ASTM D-149 | 20 | KV/mm |
| 功率系数 | 60Hz | ASTM D-150 | 0.05 | ||
| 介电定数 | 60Hz | ASTM D-150 | 4 | ||
| 抗体积系数 | ASTM D-257 | >1515 | Ω.m | ||
| 热性能 | 绵性膨胀系数 | ASTM D-696 | 6×10-5 | cm/cm/°C | |
| 热变形温度 | 18.56kg | ASTM D-648 | 90 | ℃ | |
| 维卡软化点 | 1kg | ASTM D-1525 | 90 | ℃ | |
| 热传导 | ASTM D-177 | 5×10-4 | cal/seccm?℃/cm | ||
| 燃烧度 | 1/8",1/16" | UL94 | HB | ||
| 比热 | 0.35 | cal/g/℃ | |||